Plazma elektrolitik oksitleme yöntemiyle AA7075 alüminyum alaşımı üzerine kaplanan seramik kaplamaların yapısal ve aşınma davranışı

Authors : Serdar KARAOĞLU, Ekrem SONUVAR

Pages : 405-410

View : 29 | Download : 10

Publication Date : 2017-08-18

Article Type : Research Paper

Abstract :Normal 0 false false false TR X-NONE X-NONE /* Style Definitions */ table.MsoNormalTable {mso-style-name:`Normal Tablo`; mso-tstyle-rowband-size:0; mso-tstyle-colband-size:0; mso-style-noshow:yes; mso-style-priority:99; mso-style-parent:``; mso-padding-alt:0cm 5.4pt 0cm 5.4pt; mso-para-margin-top:0cm; mso-para-margin-right:0cm; mso-para-margin-bottom:10.0pt; mso-para-margin-left:0cm; line-height:115%; mso-pagination:widow-orphan; font-size:11.0pt; font-family:`Calibri`,sans-serif; mso-ascii-font-family:Calibri; mso-ascii-theme-font:minor-latin; mso-hansi-font-family:Calibri; mso-hansi-theme-font:minor-latin; mso-bidi-font-family:`Times New Roman`; mso-bidi-theme-font:minor-bidi; mso-ansi-language:TR;} Bu çalışmada 7075 alüminyum alaşımı üzerinde, plazma elektrolitik oksitleme insert ignore into journalissuearticles values(PEO); işlemi ile seramik kaplamalar oluşturulup, akım yoğunluğunun ve elektrolit içeriğinin; kaplama yapısına, kalınlığına, yüzey pürüzlülüğüne ve aşınma davranışına etkileri araştırılmıştır. Kaplamaların mikroyapısı ve faz analizinde SEM ve XRD yöntemleri kullanılmış, kuru sürtünme şartlarında aşınma testleri, mikrosertlik ve yüzey pürüzlülüğü ölçümleri gerçekleştirilmiştir. Sonuç olarak, PEO işleminde uygulanan akım yoğunluğunun arttırılmasıyla, kaplama kalınlığının, mikrosertlik değerlerinin, yüzey pürüzlülüğünün ve aşınma direncinin arttığı görülmüştür.
Keywords : Alüminyum alaşımı, Plazma elektrolitik oksitleme PEO, Akım yoğunluğu, Aşınma