Investigation of the corrosion properties of AA5754 aluminum alloy coated with graphene oxide by the electrophoretic deposition method

Authors : Duygu Candemir, Kubilay Karacif, Levent Kartal

Pages : 10-16

View : 99 | Download : 101

Publication Date : 2024-02-29

Article Type : Research Paper

Abstract :This study aims to coat the aluminum alloy (AA5754) with graphene oxide by electrophoretic deposition (EPD) method, which is a cheap, eco-friendly, and straightforward process, and to determine the effect of the coating on the corrosion properties of the aluminum alloy. The graphene oxide coatings were characterized by X-ray diffraction (XRD), optical microscopy, and scanning electron microscopy (SEM). It was determined that the graphene oxide coatings grew layer by layer and their thickness increased with increasing time and applied potential. The effect of graphene oxide coating on the corrosion properties of AA5754 aluminum alloy was investigated by a potentiodynamic method in 3.5% NaCl environment. According to corrosion test results, it was determined that the corrosion potential of the coated AA5754 aluminum alloy changed positively, while the corrosion current and corrosion rate decreased. The highest corrosion potential was determined as -805 mV at 5 V-5 min and 7 V-3 min coating conditions. The lowest corrosion current density (9.8.10-7 A∙cm-2), and corrosion rate (0.011 mm∙y-1) were obtained at 5 V-3 min. coating conditions.
Keywords : Grafen oksit, Alüminyum, Elektroforetik biriktirme, Korozyon, Kaplama