The Effect of Boriding Temperature and Time on the Structural and Mechanical Properties of M42 Steel

Authors : Hasan Onur Tan, Selçuk Atasoy, Sitki Aktaş

Pages : 1-5

Doi:10.46810/tdfd.1437681

View : 156 | Download : 85

Publication Date : 2024-06-28

Article Type : Research Paper

Abstract :In this study, the effect of boriding temperature and time on the structural and mechanical properties of M42 high speed steel were investigated. Samples placed in Ekabor II powder were exposed to pack boriding treatment at 900°C and 1000°C for 4 hour and at 950°C for 2, 4 and 6 hours. Scanning electron microscope (SEM) images indicate that boron diffuses into the samples and a sawtooth-like cross-sectional morphology is formed. The presence of boron has also been proven by Energy Dispersive X-ray spectrometry (EDX). In addition, it was determined that boron layer thickness increased with increasing boriding temperature. When the microhardness values were examined, it was observed that the sample borided at the highest temperature had the highest hardness value and the hardness values decrease with the decreasing of boriding temperature. Similar results were also obtained regarding the boriding time. The highest microhardness and layer thickness values were obtained after 6 hours of boriding. Additionally, it was observed that the hardness values of borided samples decreased as they moved from the surface to the inner parts.
Keywords : Borlama, Borlama sıcaklığı, Borlama süresi, M42 çeliği, Mekanik özellikler

ORIGINAL ARTICLE URL