Production and Characterization Of Ti-10Cr-3,33Co-3,33Egg Shelter Composite Materials Using By Powder Metallurgy

Authors : Ahmet YÖNETKEN, Günnur PESMEN, Ayhan EROL

Pages : 158-165

Doi:10.29137/umagd.474031

View : 26 | Download : 14

Publication Date : 2020-01-31

Article Type : Research Paper

Abstract :Titanium-based intermetallic compounds are frequently used in the production of biomaterials. The behavior of titanium similar to bone mechanical properties causes the use of titanium as a biomaterial and preferred among the materials. It also makes its use attractive in industrial applications at high temperatures. TiCrCo intermetallics are known to be used together with Ti matrix materials to improve the properties of the group in addition to elements such as Cr, especially Ti, Co, Mo and Fe in various application areas. This information is used frequently in the sintering process.  In this study, Ti-10Cr-3,33Co-3,33 egg shelter powders were prepared as a sample mixture. When the properties of the samples  produced after sintering are examined, it shows the effects of Co on TiCr. 3.33% Co additive was used in the composition of the  composition and mechanical properties were determined in the produced samples. By looking at metallographic analysis,  structural features were tried to be determined. The density of the produced samples was calculated, hardness and shear strength  were determined. According to the results of the analysis, 3.33% Co composition and 3.71 gr / cm3 density, and 285.5 HV  hardness values at 1200 ° C were obtained.  In this study, Ti-10Cr-3,33Co-3,33 egg shelter powders were prepared as a sample mixture. When the properties of the samples produced after sintering are examined, it shows the effects of Co on TiCr. 3.33% Co additive was used in the composition of the composition and mechanical properties were determined in the produced samples. By looking at metallographic analysis, structural features were tried to be determined. The density of the produced samples was calculated, hardness and shear strength were determined. According to the results of the analysis, 3.33% Co composition and 3.71 gr / cm3 density, and 285.5 HV hardness values at 1200 ° C were obtained..
Keywords : Sintering, intermetallic, Egg Shelter, Composite, High temperatureSintering