THE EXPERIMENTAL INVESTIGATION OF ANNEALING PARAMETERS EFFECTS ON AL2024-T3 MATERIALS’ FORMABILITY AND MECHANICAL PROPERTIES

Authors : Mehmet Okan KABAKÇI, İbrahim KARAAĞAÇ, Mehmet Yasin DEMİREL

Pages : 338-346

Doi:10.36222/ejt.648167

View : 37 | Download : 11

Publication Date : 2019-12-30

Article Type : Research Paper

Abstract :In this study, the effects of annealing parameters on the formability and mechanical properties of Al2024-T3 sheet material were investigated experimentally. Annealing process were applied at 100 °C, 200 °C, 300 °C, 400 °C annealing temperatures and at 6 minutes, 30 minutes, 60 minutes annealing times. The forming operations were applied in 10 mm / sec deformation velocity and in V bending dies with an angle of 30 °, 60 °, 90 °, 120 °. In the experimental studies, it was determined that there was no significant change in the hardness values of the specimens at temperatures less than 300 ° C annealing temperature and 6 minutes annealing time parameters, but an irregular changes were observed in the mechanical properties of specimens. However, it was observed that there were a significant decrease in the hardness values and mechanical properties of the test specimens after the annealing temperature of 300 ° C and the annealing time of 6 minutes. It has been observed that the samples only has been formed successfully in a 30 ° die angle and at low temperatures insert ignore into journalissuearticles values(RT - 100 ° C - 200 ° C);. It has been observed that a successful forming process has been performed in 30 ° and 60 ° die angles by increasing the annealing parameters values insert ignore into journalissuearticles values(400 ° C - 30 min or 400 ° C - 60 min);. However, forming defects such as cracks and fractures were encountered in forming processes using 90 ° and 120 ° die angled.
Keywords : Al2024 T3, Annealing, Formability, Mechanical Properties

ORIGINAL ARTICLE URL