Corrosion Behavior of Graphene Nanoplatelet-Coated TiB2 Reinforced AZ91 Magnesium Matrix Semi-Ceramic Hybrid Composites

Authors : Engin ÇEVİK, Murat GÜNDOĞAN, Alper İNCESU, Muhammet TURAN

Pages : 27-33

Doi:10.17350/HJSE19030000209

View : 19 | Download : 12

Publication Date : 2021-03-31

Article Type : Research Paper

Abstract :In this study; Hybrid composites containing different proportions of TiB2 and graphene were produced using the pressure infiltration method. Inert SF6 gas is used to prevent oxidation in the productions. While 8 bar infiltration pressure was provided by argon gas, the infiltration temperature was chosen as 800°C. The corrosion behaviors of the compos-ite materials were examined. Corrosion resistance was determined by potentiodynamic and immersion corrosion testing in 3.5% NaCl solution. In addition, SEM examinations were conducted to understand the corrosion mechanisms. At the end of the measurements, the highest porosity was measured as %4,7 in composite containing 1% graphene compared to pure matrix and composite containing only TiB2. The added reinforcement insert ignore into journalissuearticles values(TiB2 and Graphene); elements cause decreases in corrosion resistance. The highest corrosion resist-ance was achieved in AZ91 alloys.
Keywords : Graphene, AZ91, TiB2, Magnesium matrix composites, Corrosion