Mechanical and microstructural characterization of rubber particle reinforced thermoplastic for automobile bumper application

Authors : Muideen Adebayo BODUDE, Theddeus Tochukwu AKANO, Adebayo Felix OWA

Pages : 89-93

View : 21 | Download : 14

Publication Date : 2019-12-25

Article Type : Research Paper

Abstract :Thermoplastic elastomer composite produced from low-density polyethylene insert ignore into journalissuearticles values(LD-PE); mixed with 150μm pulverised rubber particles in varied proportions insert ignore into journalissuearticles values(5%, 10%, 15%, 20% and 25%); using stir casting technique was characterized for mechanical properties in relation to the base polyethylene. Tensile, impact, flexural, and hardness tests were conducted to investigate the mechanical properties of the elastomer. The results obtained showed that the reinforcement with up to 20%wt of pulverised rubber particle generated a composite with a higher modulus of elasticity of 374MPa and hardness of 14.06BHN relative to those of the base material which are 227MPa and 11.48BHN respectively. However, the bending strength and the impact energy of the generated composite are 40MPa and 19.5J, which are lower than those of the base material, which are 57MPa and 20J. This may be due to insufficient adhesion between the phases of the matrix and reinforcement.
Keywords : Elastomer, automobile tyres