ASSESSING THE VOLUME FRACTIONS OF THE PHASES, NODULARITY AND NODULE COUNT OF SPHEROIDAL GRAPHITE CAST IRON USING IMAGEJ SOFTWARE

Authors : Selin TORAMAN, Tugay COSGUN, Bulent ALKAN, Baris CETİN, Oncu AKYİLDİZ

Pages : 137-142

Doi:10.22531/muglajsci.521128

View : 17 | Download : 9

Publication Date : 2019-06-30

Article Type : Research Paper

Abstract :In this study, a simple method for assessing the microstructure of ductile cast iron by using a freeware digital image processing software is described. The method is applied to three different ductile iron grades to assess their ferrite, pearlite and graphite volume fractions as well as graphite nodularity, nodule count, nodule size. All specimens were found to show good nodularity insert ignore into journalissuearticles values(~ 88 % by area); with different graphite average size and perimeter morphology. The amount of graphite was also found to be similar insert ignore into journalissuearticles values(11±2 % by area); in all specimens. On the other hand, ferrite percentages were found as 85.8, 57.1, and 52.5 % respectively for ASTM A536 grades 60-40-18, 65-45-12, and 80-55-06. It was also found that among these three grades, the higher the pearlite content, the higher the hardness. The agreement with the standards confirms that quantitative metallography through image processing is a powerful tool in order to estimate the mechanical properties of cast irons.
Keywords : Image Processing, ImageJ, Spheroidal Graphite Cast Iron