FARKLI KONSANTRASYONLARDAKİ POVİDON İYOTUN HİBRİT CAD/CAM MATERYALİNİN RENK STABİLİTESİNE ETKİSİ

Authors : Gaye SAĞLAM

Pages : 75-79

Doi:10.17567/ataunidfd.1009742

View : 17 | Download : 6

Publication Date : 2022-02-15

Article Type : Research Paper

Abstract :Amaç: Bu çalışmanın amacı, farklı konsantrasyonlardaki povidon iyot solüsyonlarının hibrit seramik CAD/CAM materyalinin renk stabilitesine etkisinin incelenmesidir. Yöntemler: Çalışmada 2M2 rengine sahip Cerasmart insert ignore into journalissuearticles values(GC Corporation, Tokyo, Japonya); hibrit seramik bilgisayar destekli tasarım/bilgisayar destekli üretim insert ignore into journalissuearticles values(CAD/CAM); bloklarından 1,5x12x12mm boyutunda 60 adet kesit elde edildi. Örneklerin başlangıç renk değerleri spektrofotometre cihazı ile CIE L*a*b* sistemine göre ölçüldü. Örnekler 24 saat süreyle bekletilecekleri solüsyonlara göre rastgele 3 gruba ayrıldı insert ignore into journalissuearticles values(n=20);. Grup 1 kontrol grubu olarak belirlendi ve örnekler distile suda bekletildi. Grup 2’de örnekler %0,25’lik povidon iyot solüsyonunda bekletildi. Grup 3’de ise örnekler %2,5’lik povidon iyot solüsyonunda bekletildi. Örnekler temizlendi ve renk değerleri tekrar ölçüldü. Renk değişim miktarları ΔE cinsinden hesaplandı. Elde edilen verilerin istatistiksel analizi Kruskal-Wallis testi ile yapıldı. Bulgular: Poivdon iyot solüsyonunda bekletilen örneklerde anlamlı derecede yüksek ΔE değerleri elde edildi insert ignore into journalissuearticles values(P < .05);. %2,5’lik povidon iyot grubu %0.25’lik povidon iyot grubuna göre anlamlı derecede daha yüksek ΔE değerleri gösterdi insert ignore into journalissuearticles values(P < .05);. %0,25’lik povidon iyot solüsyon grubunda elde edilen renk değişimi klinik olarak kabul edilebilir bulundu. Sonuç: Povidon iyot solüsyonu rezin seramik CAD/CAM materyali üzerinde renk değişimine neden olmaktadır. Povidon iyotun daha yüksek konsantrasyonunda daha fazla renk değişimi izlenmektedir. Anahtar kelimeler: hibrit seramik, CAD/CAM, povidon iyot, renk değişimi Effect of povidone iodine at different concentrations on the color stability of hybrid CAD/CAM material Abstract Objective: The aim of this study was to investigate the effect of different concentrations of povidone iodine solutions on the color stability of hybrid ceramic CAD/CAM material. Methods: In the study, 60 sections with dimensions of 1,5x12x12mm were obtained from Cerasmart insert ignore into journalissuearticles values(GC Corporation, Tokyo, Japan); hybrid ceramic computer aided desing/computer aided manufacturing insert ignore into journalissuearticles values(CAD/CAM); blocks with 2M2 color. The initial color values of the sections were measured with a spectrophotometer device according to the CIE L*a*b* system. Samples were randomly divided into 3 groups according to the solutions that they strored for 24 hours insert ignore into journalissuearticles values(n=20);. Group 1 was determined as a control group and samples were kept in distilled water. In group 2, samples were kept in 0,25% povidone iodine solution. In group 3, samples were kept in 2,5% povidone iodine solution. The samples were cleaned and the color values were measured again. Color changes were calculated in ΔE. Statistical analysis of the data obtained was made using the Kruskal-Wallis test. Results: Significantly higher ΔE values were obtained in samples kept in povidone iodine solution insert ignore into journalissuearticles values(P < .05);. The 2,5% povidone iodine group showed significantly higher ΔE values than the 0,25% povidone iodine group insert ignore into journalissuearticles values(P < .05);. The color change obtained in the 0,25% povidone iodine solution group was found clinically acceptable. Conclusion: Povidone iodine solution caused color change on the resin ceramic CAD/CAM material. More color change was observed at higher concentrations of povidone iodine. Keywords: hybrid ceramic, povidone iodine, color change
Keywords : hibrit seramik, CAD CAM, povidon iyot, renk değişimi