TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL

TRIBOCORROSION PROPERTIES OF BORIDED AND Al2O3-COATED NiTi MATERIAL

Pages : 873-884

View : 24 | Download : 12

Publication Date : 2022-12-30

Article Type : Research Paper

Abstract :The purpose of this study was to investigate the tribological properties of NiTi shape-memory alloy that was borided and coated with Al2O3 using the electrophoretic deposition insert ignore into journalissuearticles values(EPD); method. For the study, the sample surface was borided for 1 and 4 h at 800°C with the method of pack boriding, and the surface of the sample that was borided was coated with Al2O3 using the EPD method. The tribocorrosion properties of the untreated samples, borided samples, and borided and insert ignore into journalissuearticles values(duplex); Al2O3-coated samples were investigated and characterized using XRD and SEM devices. Accordingly, following the boriding treatment on the NiTi material, Al2O3 coating was successfully carried out with the EPD method. In comparison to the untreated samples, the tribocorrosion resistance of the surface-treated samples under a load of 3 N in a 3.5% NaCl solution increased. Additionally, among all samples, those that were subjected to the duplex surface treatment had the best tribocorrosion properties.
Keywords : NiTi, Boriding, EPD, Tribocorrosion

ORIGINAL ARTICLE URL

* There may have been changes in the journal, article,conference, book, preprint etc. informations. Therefore, it would be appropriate to follow the information on the official page of the source. The information here is shared for informational purposes. IAD is not responsible for incorrect or missing information.