Post-Ultraviolet-Curing Process Effects on Low-Velocity Impact Response of 3D Printed Polylactic Acid Parts

Authors : Tarkan Akderya

Pages : 943-955

Doi:10.16984/saufenbilder.1279767

View : 220 | Download : 219

Publication Date : 2023-10-18

Article Type : Research Paper

Abstract :In this study, polylactic acid (PLA) parts produced with the 3D fused deposition modelling (FDM) technique were cured with ultraviolet irradiation (post-UV-curing) after production, and the low-velocity impact behaviour of the parts was experimentally investigated. Accordingly, PLA parts were subjected to post-UV-curing at 15-, 30-, 45-, and 60-minute periods. The impact behaviour of the specimens produced with production parameters of 200 °C printing temperature, 0.2 mm layer thickness, 50 mm/s printing speed, 100% infill rate, and 45° raster angle was compared with the raw specimens after the post-UV-curing process was applied. As a result of the impact tests, peak force, peak displacement, peak energy, and puncture energy values were obtained from the force-displacement graphs. It has been revealed that the post-UV-curing implementation increases the peak force values of PLA specimens and decreases the displacement values compared to the raw specimens. All specimens\' impact behaviour improves with the post-UV-curing process; however, a decreasing trend is entered after 30 min.
Keywords : FDM, UV irradiation, polylactic acid, impact response, 3D printing

ORIGINAL ARTICLE URL