Investigation of Hardox 400 Steel Exposed to Heat Treatment Processes in WEDM

Investigation of Hardox 400 Steel Exposed to Heat Treatment Processes in WEDM

Pages : 237-244

View : 37 | Download : 6

Publication Date : 2019-03-01

Article Type : Research Paper

Abstract :In this study, microstructure, mechanical, and conductivity characteristics of Hardox 400 steel were changed with different heat treatments and effect of such characteristics on its machinability with Wire Electrical Discharge Machining insert ignore into journalissuearticles values(WEDM);. Optical microscope examinations were performed to determine various characteristics, and additionally microhardness and conductivity measurements were conducted hereof. L18 Taquchi test design was conducted with three levels and four different parameters to determine the effect of such alterations on its machinability with WEDM and post-processing Cutting width insert ignore into journalissuearticles values(kerf);, Surface roughness insert ignore into journalissuearticles values(Ra);, Material removal rate insert ignore into journalissuearticles values(MRR); values were determined. Micro changes were ensured successfully by using applied heat treatments. The best kerf value was obtained from sample 6 which was tempered from 350 °C. The microstructure of this sample was composed of commonly α ferrite and few pearlites. The best Ra value was obtained from sample 3 which was tempered from 200 °C. The microstructure of this sample was composed of few α ferrite and commonly pearlites. The best MRR value was obtained from sample 5 which was tempered from 300 °C. The microstructure of this sample was composed of almost equally α ferrite and pearlites. Additionally t he most effective parameters on Ra were determined as hardox and current. The most effective parameters on kerf and MRR were determined as time off and hardox.
Keywords : Hardox steel, heat treatment, microstructure, WEDM, kerf, Ra, MRR

ORIGINAL ARTICLE URL

* There may have been changes in the journal, article,conference, book, preprint etc. informations. Therefore, it would be appropriate to follow the information on the official page of the source. The information here is shared for informational purposes. IAD is not responsible for incorrect or missing information.