Thermal storage of (solar) energy by sorption of water in magnesium (hydro) carbonates

Authors : Rickard ERLUND, Ron ZEVENHOVEN

Pages : 102-109

Doi:10.5541/eoguijt.324161

View : 14 | Download : 5

Publication Date : 2017-05-31

Article Type : Research Paper

Abstract :In this paper the thermodynamic properties and the chemical reaction kinetics of the reversible reactions where sorption of water in magnesium hydro carbonates are analysed for thermal energy storage insert ignore into journalissuearticles values(TES);. Depending on the conditions mainly nesquehonite, lansfordite and hydromagnesite may be formed from magnesite, all with a certain heat effect. Magnesite and water vapour can form nesquehonite or lansfordite via reaction insert ignore into journalissuearticles values(R1); and insert ignore into journalissuearticles values(R2);: MgCO3 + 3H2Oinsert ignore into journalissuearticles values(g); ↔ MgCO3∙3H2O ΔH = -1.83 MJ/kg MgCO3, T=298K insert ignore into journalissuearticles values(R1); MgCO3 + 5H2Oinsert ignore into journalissuearticles values(g); ↔MgCO3∙5H2O ΔH = -2.54 MJ/kg MgCO3, T=298K insert ignore into journalissuearticles values(R2); Compared to other chemical sorption compounds, its advantages are low operating temperatures while they can act as a fire retardant. Experimental data is presented on the reactivity of the dehydration at various temperatures. The rate of dehydration of the nesquehonite is sufficient at low temperatures such as 50 °C and the reaction is about 90 % completed after 120 minutes. Magnesite reaches partial re-hydration to about 37% conversion after 24 hours. For better contact between reagents, mixtures with silica gel were used. A too large amount of water vapour, causing condensation of the water, appears to make the reactions irreversible. The temperatures of operating the process are presented as well as which compounds give an optimal energy storage.
Keywords : Thermal Energy Storage, Magnesium carbonate, Reversible reaction, Nesquehonite