Biodegradability of degradable mulching film in a laboratory-controlled composting test

Authors : Xuemei ZHANG, Yaxi HUANG, Deqiang LI, Zicheng WEN, Baoxun SUI, Zhiyong LIU

Pages : 859-866

Doi:10.3906/kim-1208-19

View : 19 | Download : 9

Publication Date : 0000-00-00

Article Type : Research Paper

Abstract :A series of degradable films was prepared, and 2 formulas of polyethylene insert ignore into journalissuearticles values(PE); films with the highest degradable performance were experimentally determined. These films contained 3.43% and 0.44% stearate, and were denoted as PE-3 and PE-4, respectively. Their biodegradability was studied in a laboratory-controlled composting test using ordinary PE film insert ignore into journalissuearticles values(OPEF); as a control. Contrast composting experiments indicated that the biodegradability of untreated samples was very low, and that the biodegradation rates of PE films after natural aging were significantly higher. FT-IR analysis showed that OPEF changed little after the composting experiment, and that PE-3 and PE-4 showed a carbonyl absorption peak at 1720 cm-1, whose intensity increased with increased composting time. Analysis of the viscometric-average molecular weight revealed that it changed little for untreated film but significantly decreased for aged films, especially PE-3, after the composting experiments.
Keywords : Resulting polyethylene film, biodegradability, composting