PROTEZ TEMİZLEYİCİ SOLÜSYONLARIN ISI İLE POLİMERİZE OLAN AKRİLİK REZİNİN MİKROSERTLİĞİNE ETKİSİ

Authors : Özgür ÖZTÜRK, Mürşide GÜLTEKİN

Pages : 7-11

Doi:10.17567/ataunidfd.307087

View : 14 | Download : 9

Publication Date : 2017-04-16

Article Type : Research Paper

Abstract :Amaç: Bu çalışmanın amacı; protez temizleyici solüsyonların ısı ile polimerize olan akrilik rezinin mikrosertliği üzerine etkisini incelemektir. Gereç ve Yöntem: 50 akrilik rezin örnek insert ignore into journalissuearticles values(15 mm × 15 mm × 3 mm); hazırlandı. Örnekler rastgele dağıtılarak, sıralanan solüsyonlara göre gruplara ayrıldı:   % 0.2 klorheksidin glukonat, %0.5 sodyum hipoklorit insert ignore into journalissuearticles values(NaOCl);, %1 NaOCl, alkalin peroksit tablet solüsyonu insert ignore into journalissuearticles values(n=10);. Kontrol grubu örnekler distile suda bekletildi. Solüsyonlarda bir daldırma 20-dakika olarak belirlendi. Her bir örneğin Vickers sertlik değeri mikrosertlik cihazı ile daldırma öncesi ve 720 daldırma sonrası ölçülerek karşılaştırıldı.   Veriler SPSS 15.0 programına taşınarak eşleştirilmiş örneklemler t-testi, tek yönlü varyans analizi ve Tukey HSD testi ile gruplar arası karşılaştırmalar yapıldı insert ignore into journalissuearticles values(p< 0.05);. Bulgular: Bulgular alkalin peroksit tablet solüsyonunun akrilik rezinin mikrosertliğinde istatistiksel olarak anlamlı azalmaya yol açtığını göstermiştir. Çalışmada test edilen diğer solüsyonlar akrilik rezinin mikrosertliği üzerinde anlamlı bir etkiye neden olmamıştır. Sonuç: Alkalin peroksit tablet solüsyonu hariç distile su, %0.2 klorheksidin glukonat, % 0.5 NaOCl ve %1 NaOCl solüsyonları günde 20 dakika kullanımı taklit eden 720 kullanım periyodunda ısı ile polimerize olan akrilik rezinin mikrosertliğini anlamlı olarak etkilememiştir Anahtar kelimeler: Diş protezi, Protez temizleyicileri, Sağlamlık testleri, Akrilik rezinler   EFFECT OF DENTURE CLEANSING SOLUTIONS ON MICROHARDNESS OF A HEAT-CURE ACRYLIC RESIN Aim: The aim of this study was to investigate the influence of denture cleansing solutions on micro hardness of a heat-cure acrylic resin. Materials and Methods: Fifty specimens insert ignore into journalissuearticles values(15 mm × 15 mm × 3 mm); were prepared with a heat-cure acrylic resin. Specimens were randomly distributed into groups and immersed in the following solutions: 0.5% sodium hypochlorite insert ignore into journalissuearticles values(NaOCl);, 1% NaOCl, alkaline peroxide tablet solution and, 0.2% chlorhexidine gluconate. The control group was immersed in distilled water. An immersion was detected 20-minute for all solutions. The microhardness value of each specimen was obtained using the microhardness testing machine recording the Vickers hardness number before the beginning of the immersion cycles and after completion of 720 immersion cycles and compared. Data were imported to SPSS 15.0 software and were analyzed by paired t-test and One-Way ANOVA and Tukey HSD test were used for comparison among groups insert ignore into journalissuearticles values(p< 0.05);. Results: The results show that alkaline peroxide tablet solution caused the statistically significant reduction of the microhardness of the acrylic resin. Other solutions tested in this study did not cause a significant effect on the microhardness of the acrylic resin. Conclusions: It was concluded that immersion in distilled water, chlorhexidine gluconate, 0.5% NaOCl and, 1% NaOCl solutions, simulating 720 days of 20 min daily soaking did not cause clinically significant adverse effects on the microhardness of the heat-polymerized acrylic resin, except for the alkaline peroxide tablet solutions. Keywords: Dental Prostheses, Denture Cleansers, Hardness Tests, Acrylic Resins
Keywords : Diş protezi, Protez temizleyicileri, Sağlamlık testleri